Description
Details
Grade:HP (High Pure)
Application:Liners Of Industrial Furnace
Thickness:6-50mm
Width:610/1220mm
Length:3600/7200/14640mm
Chemical Composition:AL2O3+SIO2
Ultimate Strength (≥ MPa):0.08-0.12Mpa
Working Temperature:1100C/1260C/1360C/1430C (2012F/2300F/2480F/2600F)
Fiber Diameter:3-5um
Shrinkage (1800 ℉, 3h):3%(24 Hours)
Thermal Conductivity:0.09-0.16
Density (kg/m³ ):128
Characteristic :
Ceramic fiber blanket made from common, high pure, zircon, chromic aluminum silicate fiber, after the process of needling, thermoforming, crossbar cutting, rolling up ,etc. which is through double-sided needling operation by using spun technology.
Low heat strong capacity, Low thermal conductivity
Excellent thermal stability and shock resistance, resist devitrification at high temperature
Excellent tearing resistant
Excellent insulating performance, fire prevention and sound absorption
Application
All kinds of industrial kiln linings(hot surface and back lining)
Furnace body expansion joint, furnace door, top cap seals
Grade:HP (High Pure)
Application:Liners Of Industrial Furnace
Thickness:6-50mm
Width:610/1220mm
Length:3600/7200/14640mm
Chemical Composition:AL2O3+SIO2
Ultimate Strength (≥ MPa):0.08-0.12Mpa
Working Temperature:1100C/1260C/1360C/1430C (2012F/2300F/2480F/2600F)
Fiber Diameter:3-5um
Shrinkage (1800 ℉, 3h):3%(24 Hours)
Thermal Conductivity:0.09-0.16
Density (kg/m³ ):128
Characteristic :
Ceramic fiber blanket made from common, high pure, zircon, chromic aluminum silicate fiber, after the process of needling, thermoforming, crossbar cutting, rolling up ,etc. which is through double-sided needling operation by using spun technology.
Low heat strong capacity, Low thermal conductivity
Excellent thermal stability and shock resistance, resist devitrification at high temperature
Excellent tearing resistant
Excellent insulating performance, fire prevention and sound absorption
Application
All kinds of industrial kiln linings(hot surface and back lining)
Furnace body expansion joint, furnace door, top cap seals
High building fire proof and heat insulation.